FKM Food Grade Orings Waterproof , Industrial O Ring Excellent Chemical Resistance
FKM® or fluorocarbon elastomers were first introduced in the mid 1950's. Since then they have become of major importance in the seal industry. Due to its good chemical resistance, high temperature range and its low compression set, fluorocarbon rubber is the most significant single elastomer development in recent history. The working temperature range ifor FKM® is considered to be -15 to +400 degrees F (-29 to +204 degrees C), but it will take temperatures up to 600 degrees F (316 degrees C) for short periods of time. Du Pont's Kalrez® is normally recommended up to 500 degrees F (260 degrees C). On the low end, FKM® compounds have been known to seal at -65 degrees F (-54 degrees C) in some special static applications, however the normal low temperature limit is -15 degrees F (-26 degrees C). Fluorocarbon 0-rings should be considered for seal use in aircraft, automobile, scientific instruments and other mechanical devices requiring maximum resistance to elevated temperature and to many functional fluids. They are widely used in diffusion pumps on vacuum systems and on vacuum flanges on mass spectrometers and electron microscopes. FKM® is recommended for most applications and Kalrez® is only used where the additional temperature range can be justified by the increased cost.
FKM® and Kalrez® are recommended for:
FKM is not recommended for:
|
ORIENTAL STAR TEST REPORT | |||
V7501 COMPOUND | |||
ASTM D2000 M2HK 710 A1-10 B37 B38 EO78 EF31 F13 Z=Hardness 75±5 | |||
Press Cure | |||
Sheet : 5min 175℃ | |||
Button : 10 min 175℃ | |||
ORIGINAL PROPERTIES | SPECIFICATION | TEST RESULT | |
HARDNESS SHORE A | 75°±5 | 73 | |
TENSILE STRENGTH, MPA, MIN | 10 | 10.9 | |
ULTIMATE ELONGATION, %, MIN | 150 | 213 | |
SPECIFIC GRAVITY (g/cm3) | 1.85+/-0.08 | 1.87 | |
HEAT RESISTANCE 70 H . AT 250℃(A1-10) | |||
CHANGE IN HARDNESS, POINTS | +10 | +5 | |
CHANGE IN TENSILES STRENGTH, % | -25 | +26 | |
CHANGE IN ULTIMATE ELONGATION,MAX % | -25 | -18 | |
COMPRESSION SET, MAX, 22H AT 175℃ (B37 ) | 50 | 21.5 | |
COMPRESSION SET, MAX, 22H AT 200℃ (B38 ) | 50 | 28.3 | |
FLUID RESISTANCE FUEL.101. 70H AT 200℃ (EO78) | |||
CHANGE IN HARDNESS, POINTS | -15~+5 | -13 | |
CHANGE IN TENSILES STRENGTH, MAX % | -40 | -20.7 | |
CHANGE IN ULTIMATE ELONGATION,MAX % | -20 | -8.3 | |
CHANGE IN VOLUME % | 0~+15 | +10.5 | |
FLUID RESISTANCE FUEL C, 70H AT 23℃(EF31) | |||
CHANGE IN HARDNESS, POINTS | ±5 | -4 | |
CHANGE IN TENSILES STRENGTH, MAX % | -25 | -20.2 | |
CHANGE IN ULTIMATE ELONGATION,MAX % | -20 | -18.6 | |
CHANGE IN VOLUME % | 0~+10 | +5 |